Pathologie Fissuration

FISSURES DUES AU TASSEMENT DU BETON FRAIS LOCALISATION DE LA PHATOLOGIE FISSURES DUES AU TASSEMENT DU BETON FRAIS

DESCRIPTION DE LA PATHOLOGIE RESSUAGE ET SEGREGATION - SE MANIFESTE AVANT LA PRISE - APPARITION D’UNE PELLICULE D’EAU A LA SURFACE LIBRE HORIZONTALE DU BETON FRAIS - TASSEMENT PROGRESSIF DU SQUELETTE SOUS L’EFFET DE LA PESANTEUR - DANS LES CAS EXTREMES, CREATION DE FISSURES OUVERTES AU DROIT DES OBSTACLES QUI S ’OPPOSENT AUX MOUVEMENTS DE TASSEMENT DU BETON (armatures, variations locales d ’épaisseur…)

FISSURES DUES AU RETRAIT PLASTIQUE LOCALISATION DE LA PHATOLOGIE FISSURES DUES AU RETRAIT PLASTIQUE

VISUALISATION DE LA PATHOLOGIE RETRAIT PLASTIQUE - DESSICATION

VISUALISATION DE LA PATHOLOGIE RETRAIT PLASTIQUE - DESSICATION SURFACE 0.5 à 2 mm d’épaisseur

DESCRIPTION DE LA PATHOLOGIE RETRAIT PLASTIQUE - DESSICATION - PRINCIPALEMENT LOCALISE SUR LES PIECES MINCES OU SUR LES GRANDES SURFACES HORIZONTALES EN CONTACT AVEC L’AIR - RETRAIT DU BETON FRAIS OU EN COURS DE PRISE LORSQU’IL EST ENCORE DANS UN ETAT AISEMENT DEFORMABLE (avant et pendant la prise pendant un temps limité) - RETRAIT D’ORIGINE EXOGENE PAR DESSICCATION (évaporation)

DESCRIPTION DE LA PATHOLOGIE RETRAIT PLASTIQUE - DESSICATION FACTEUR AGGRAVANT :

FISSURES DUES AU RETRAIT THERMIQUE LOCALISATION DE LA PHATOLOGIE FISSURES DUES AU RETRAIT THERMIQUE

VISUALISATION DE LA PATHOLOGIE RETRAIT THERMIQUE

DESCRIPTION DE LA PATHOLOGIE RETRAIT THERMIQUE - PRINCIPALEMENT LOCALISE SUR LES OUVRAGES MASSIFS ET PEU SUR LES PIECES MINCES - ECHAUFFEMENTS IMPORTANTS (> 70 °C) OCCASIONNANT UNE EXPANSION SUIVIE D’UNE CONTRACTION AU REFROIDISSMENT - LA CONTRACTION SE MANIFESTE DANS UN LAPS DE TEMPS VARIANT DE QUELQUES DIZAINES D’HEURES A QUELQUES SEMAINES APRES LA MISE EN ŒUVRE DU BETON - FISSURES PROFONDES TRAVERSANT LA TOTALITE DE L’EPAISSEUR DU BETON

FISSURES DUES AU RETRAIT HYDRAULIQUE LOCALISATION DE LA PATHOLOGIE FISSURES DUES AU RETRAIT HYDRAULIQUE

VISUALISATION DE LA PATHOLOGIE RETRAIT HYDRAULIQUE

VISUALISATION DE LA PATHOLOGIE RETRAIT HYDRAULIQUE

VISUALISATION DE LA PATHOLOGIE RETRAIT HYDRAULIQUE FISSURES SOUVENT BORDEES DE CALCITE (diffusion puis carbonatation de la chaux)

DESCRIPTION DE LA PATHOLOGIE RETRAIT HYDRAULIQUE - APPARAÎT D’AUTANT PLUS RAPIDEMENT QUE LA PIECE EST MINCE - RETRAIT LENT DU BETON DURCI PAR PERTE D ’EAU : MIGRATION PAR CAPILLARITE DE L’EAU DES ZONES HUMIDES VERS LES ZONES SECHES (favorisé par lorsque l’humidité relative est faible) - CE RETRAIT COMMENCE AU DECOFFRAGE, PROGRESSE ENTRE 1 ET 28 JOURS ET DOUBLE EN PASSANT DE 1 MOIS A 3 ANS - FISSURES INESTHETIQUES QUI S’OUVRENT AVEC LE TEMPS, COMPROMETANT QUE TRES PEU LA RESISTANCE DE L ’OUVRAGE CAR ELLES SONT PEU PROFONDES

FISSURES DUES A LA CORROSION DES ARMATURES LOCALISATION DE LA PATHOLOGIE FISSURES DUES A LA CORROSION DES ARMATURES

LA CORROSION DES ARMATURES EST SOUVENT LIEE A LA CARBONATATION VISUALISATION DE LA PATHOLOGIE CARBONATATION - CORROSION DES ARMATURES LA CORROSION DES ARMATURES EST SOUVENT LIEE A LA CARBONATATION

VISUALISATION DE LA PATHOLOGIE CARBONATATION - CORROSION DES ARMATURES

VISUALISATION DE LA PATHOLOGIE CARBONATATION - CORROSION DES ARMATURES

VISUALISATION DE LA PATHOLOGIE CARBONATATION - CORROSION DES ARMATURES

VISUALISATION DE LA PATHOLOGIE CARBONATATION - CORROSION DES ARMATURES

VISUALISATION DE LA PATHOLOGIE CARBONATATION - CORROSION DES ARMATURES

DESCRIPTION DE LA PATHOLOGIE CARBONATATION - CORROSION DES ARMATURES - CAUSES PRINCIPALES : BETON POREUX, RECOUVREMENT INSUFFISANT DES ARMATURES, CURE NEGLIGEE, ENVIRONNEMENT HUMIDE RICHE EN CO2 - NEUTRALISATION PROGRESSIVE DE L’ALCALINITE DU BETON ET POUR UN pH < 9-10, DEPASSIVATION DES ARMATURES : FORMATION DE ROUILLE (l’acier en rouillant augmente son volume de 4 fois environ) - LA CORROSION DEBUTE LORSQUE L’HUMIDITE ET L’OXYGENE PARVIENNENT AUX ARMATURES - DEFAUTS ESTHETIQUES AU DEBUT (TACHE DE ROUILLE) QUI PEUT CONDUIRE A LA RUINE DE L’OUVRAGE QUAND LE PHENOMENE SE GENERALISE

DESCRIPTION DE LA PATHOLOGIE CARBONATATION - CORROSION DES ARMATURES - FACTEUR AGGRAVANT : ENVIRONNEMENT MARIN SEL DE DEVERGLACAGE

FISSURES DUES A LA REACTION ALCALI-GRANULATS LOCALISATION DE LA PATHOLOGIE FISSURES DUES A LA REACTION ALCALI-GRANULATS

VISUALISATION DE LA PATHOLOGIE REACTION ALCALI-GRANULATS

VISUALISATION DE LA PATHOLOGIE REACTION ALCALI-GRANULATS

VISUALISATION DE LA PATHOLOGIE REACTION ALCALI-GRANULATS Gel expansif (2) au contact du granulat siliceux Gel de silice Dépôt de cristaux de silicate alcalin sur le granulat siliceux

VISUALISATION DE LA PATHOLOGIE REACTION ALCALI-GRANULATS

DESCRIPTION DE LA PATHOLOGIE REACTION ALCALI-GRANULATS - REACTION ENTRE LES ALCALINS PRESENTS DANS LE BETON ET LES GRANULATS SILICEUX REACTIFS - FORMATION D’UN GEL EXPANSIF A BASE DE SILICATE DE CALCIUM LORSQUE TROIS CONDITIONS SONT REUNIES : PRESENCE D’ALCALIS SOLUBLES, DE GRANULATS REACTIFS ET D’UNE FORTE HUMIDITE (HR > 80 %). - LA FISSURATION (RESEAUX DE FAÏENCAGE) APPARAÎT APRES DES DUREES VARIABLES (DE QUELQUES MOIS A 3 ANS OU PLUS SI L ’ENVIRONNEMENT EVOLUE) - LA FISSURATION INITIALE INESTHETIQUE CONDUIT PROGRESSIVEMENT A LA BAISSE DES PERFORMANCES DU BETON ET UNE DIMINUTION DE LA DURABILITE. LA DESTRUCTION DE L’OUVRAGE RESTE EXCEPTIONNELLE.

FISSURES DUES A LA DEFORMATION SOUS CHARGE LOCALISATION DE LA PATHOLOGIE FISSURES DUES A LA DEFORMATION SOUS CHARGE

VISUALISATION DE LA PATHOLOGIE FLUAGE

DESCRIPTION DE LA PATHOLOGIE FLUAGE - LORSQU’UNE CHARGE EST APPLIQUEE SUR LE BETON, IL SE DEFORME LENTEMENT - LORSQUE LES CONTRAINTES ENGENDREES PAR LE FLUAGE DEVIENNENT EXCESSIVES, LE BETON SE FISSURE. IL EXISTE UN FLUAGE POUR TOUTES SOLLICITATIONS : COMPRESSION, TRACTION, FLEXION, TORSION... - LA FISSURATION APPARAÎT APRES PLUSIEURS MOIS AVEC DES CONSEQUENCES IMPORTANTES - LE FLUAGE EST D ’AUTANT PLUS FAIBLE QUE LE BETON A DE PLUS FORTES RESISTANCES MECANIQUES

PRESENTATION DE LA PATHOLOGIE

VISUALISATION DE LA PATHOLOGIE DEFAUT DE RESISTANCES MECANIQUES Rupture en compression d’un poteau survenue à un endroit faible (nid de cailloux) Rupture en traction (flexion) d’une poutre survenue à un endroit faible (mauvais recouvrement de armatures)

VISUALISATION DE LA PATHOLOGIE GONFLEMENT

VISUALISATION DE LA PATHOLOGIE GONFLEMENT

DESCRIPTION DE LA PATHOLOGIE GONFLEMENT - LE GONFLEMENT DU BETON PEUT ETRE PRODUIT PAR DES MINERAUX EXPANSIFS (excès de gypse, chaux libre, magnésie), LA REACTION ALCALI-GRANULATS ET UNE AGRESSION DU MILIEU EXTERIEUR (sulfates, gel, corrosion des armatures) - LES FISSURES DE GONFLEMENT SONT D’ABORD INESTHETIQUES MAIS COMPROMETTENT A TERME LA DURABILITE DE L’OUVRAGE - LA FISSURATION APPARAÎT DES LORS QUE LES CONTRAINTES DEVIENNENT SUPERIEURES A LA RESISTANCE EN TRACTION DU BETON